Quote:
Originally Posted by EEpro
It's not going to happen. It requires high concentrations of chemicals (including boiling in chlorides) to cause any damage to 904L.
Example case: It can be boiled in 26% sodium chloride solution for 1000 hours without stress corrosion cracking.
It's of no concern at all.
|
100% correct. Materials Science background here. There is NO advantage to 904 over 316 except when exposed to very concentrated industrial acids, certainly not sweat. Just advertising.